The material PA3200GF is a glass bead-filled white polyamide 12. Laser-sintered components made from this material are very dimensionally stable and exhibit high rigidity. Compared to an unfilled PA12, the material has an improved temperature property profile, meaning that additively manufactured components made from this material still exhibit good dimensional stability even at higher temperatures. The material PA3200GF is also used for components that have to meet high requirements in terms of wear resistance and abrasion resistance.
At a glance |
Optional finishing |
|
|
Technical data PA3200GF
|
Color |
white |
|
Tensile modulus (x-y-plane) [MPa] |
3200 |
|
Tensile strength (x-y-plane) [MPa] |
51 |
|
Elongation at break (x-y-plane) [%] |
9 |
|
Melting temperature (20 °C/min) [°C] |
176 |
|
Heat deflection temperature (1.80 MPa) [°C] |
96 |
|
Heat deflection temperature (0.45 MPa) [°C] |
157 |
|
Charpy Impact Strength (x-plane) (23 °C) [kJ/m2] |
35 |
|
Density [kg/m³] |
1220 |
|
Manufacturer |
EOS GmbH |